Series 72
Endura-Shield
This product has been discontinued. Please contact your local sales representative for further assistance.
Generic Type
Aliphatic Acrylic Polyurethane
Common Usage
A durable topcoat for commercial, industrial, and marine applications that is highly resistant to abrasion, wet conditions, corrosive fumes, chemical contact and has excellent resistance to exterior weathering. Direct-to-Metal capability allows for a labor-saving, high-build, single coat application.
Recommended DFT
Topcoat Service: 2.0 to 5.0 mils (50 to 125 microns) per coat.
Direct to Metal; Over Zinc or MIO-Zinc: 3.5 to 5.0 mils (90 to 125 microns).
Note: Number of coats and thickness requirements will vary with substrate, application method and exposure. For DTM or applications over zinc or MIO-zinc, as part of a two-coat system, consult the latest version of Tnemec Technical Bulletin 13-100 or contact your Tnemec representative.
HAPS
Unthinned: 0.16 lbs/gal solids
Thinned 10% (Max) (No. 39 Thinner): 0.16 lbs/gal solids
Thinned 10% (Max) (No. 49 Thinner): 0.16 lbs/gal solids
Volume Solids
61.0 ± 2.0% (mixed) †
Colors
Refer to Tnemec Color Guide. Note: Certain colors may require multiple coats depending on method of application and finish coat color. When feasible, the preceding coat should be in the same color family (blue, gray, etc.), but noticeably different.
Finish
Gloss
Theoretical Coverage
978 mil sq ft/gal (24.0 m²/L at 25 microns) †
Number of Components
Two: Part A and Part B
Volatile Organic Compounds
Unthinned: 1.95 lbs/gallon (234 grams/litre)
Thinned 10% (Max) (No. 39 Thinner): 2.40 lbs/gallon (288 grams/litre)
Thinned 10% (Max) (No. 49 Thinner): 1.95 lbs/gallon (234 grams/litre) †
Primers
Steel: Series 1, 20, 27, 27WB, 37H, 66, L69, L69F, N69, N69F, V69, V69F, 90-97, 91-H₂O, 94-H₂O, 135, L140, L140F, N140, N140F, V140, V140F, 161, 394, V530
Note: Series V530 exterior exposed more than 24 hours, Series 135 exterior exposed more than two months, or Series N69 or N140 exterior exposed more than three months must first be scarified or reprimed with themselves. Brush blasting with fine abrasive is the preferred method of scarification. Recoat windows for other primers may apply. See those data sheets for additional information.
Curing Time
| Temperature | To Touch | To Handle | To Recoat |
|---|---|---|---|
| 75°F (24°C) | 1 hour | 5-8 hours | 12 hours |
Curing time varies with surface temperature, air movement, humidity and film thickness. Note: For faster curing and low-temperature applications, add No. 44-710 Urethane Accelerator.