Series 208
Epoxoprime MVT
Generic Type
Modified Polyamine Epoxy
Common Usage
Epoxoprime MVT is a unique, moisture-tolerant, two component, low viscosity, high solids epoxy primer designed to reduce moisture vapor emissions and provide alkalinity control for concrete with elevated moisture vapor transmission levels that exceed the acceptable limits of non-breathing resilient and polymer floor topping finishes. Epoxoprime MVT can be applied to properly prepared, 10 day old concrete and withstands moisture vapor transmission up to 15 lbs (per ASTM F 1869) and relative humidity up to 95% (per ASTM F 2170). Epoxoprime MVT has a low perm rating (0.05 perm) and is alkaline insensitive to pH levels of 14.
Special Qualifications
Series 208 was tested in accordance with, and passed, the California Department of Public Health CDPH/EHLB/Standard
Method Version 1.1, 2010 emissions testing and meets qualifications of LEED v4, Collaborative for High Performance
Schools, and Living Building Challenge.
Contact your sales reps for quotes, problem solving advice, extensive technical knowledge, pricing, ordering and field support.
Number of Components
Two: Part A and Part B (2 Parts A to 1 Part B by volume)
Volatile Organic Compounds
0.09 lbs/gallon (11 grams/litre)
Surfacer/Filler/Patcher
Series 208 mixed with fumed silica may be used for small patches or crack repairs. Certain high-early strength, cementious repair mortars are also acceptable for deeper filling and patching. Contact Tnemec for further qualifications.
Topcoats
Series 201, 205, 206, 206SC, 210, 222, 223, 224, 233, 237, 237SC, 238, 239, 239SC, 247, 248, 280, 280FC, 281, 282, 290, 291, 294, 295, 296, 297. Note: Refer to the applicable topcoat data sheet for color availability and additional information. Note: If Series 247 (tinted), 248 (tinted), 290, 291 or 297 is selected for the finish coat, Series 208 must be tinted or a tinted intermediate coat must be utilized.
Theoretical Coverage
1,604 mil sq ft/gal (39.4 m²/L at 25 microns). See APPLICATION for coverage rates.
HAPS
0.0 lbs/gal solids
Recommended DFT
16.0 to 20.0 mils (406 to 508 microns) per coat. Note: The potential for outgassing increases with higher film thickness. Care should be taken during application to reduce these occurrences. Reference the application section of this product datasheet for important information on environmental requirements.
Volume Solids
100% (mixed)
Curing Time
| Temperature | To Topcoat | Max Recoat |
|---|---|---|
| 75°F (24°C) | 6-8 hours | 24 hours |
Note: If more than 24 hours have elapsed between coats, the coated surface must be mechanically abraded before
topcoating. Note: If Series 208 is used as the primer for an epoxy mortar system, the 208 primer must be reprimed with Series 201 or 237 prior to placing the mortar. The mortar application should take place while the Series 201 or 237 is still tacky, typically up to four hours, otherwise, aggregate should be lightly broadcast into the 201 or 237 primer while wet so to provide anchor points for the trowel application. Do not broadcast aggregate into the Series 208 Epoxoprime MVT.