Series 1224
Epoxoline WB
Generic Type
Inorganic Hybrid Water-Based Epoxy
Common Usage
An advanced generation, low odor, low VOC, water-based epoxy coating featuring HydroLink curing technology for exceptional durability and corrosion resistance. Used as a primer or intermediate coat on structural steel, infrastructure, institutional, and architectural applications. Offers superior wetting for marginally prepared steel and tightly adhered existing coatings. This coating is ideally suited for steel fabrication and OEM applications, with fast-curing and rapid-handling properties. Excellent resistance to yellowing and chalking when exposed to UV and an extended recoat window make it a versatile choice. Its high-performance formulation offers excellent adhesion and provides exceptional protection up to 400°F (204°C). Formula protected under U.S. patent. Note: This product is a direct replacement for Series 27WB Typoxy.
Special Qualifications
Series 1224 meets the requirements of LEED-Low-Emitting Materials, Collaborative for High-Performance Schools-Paints & Coatings, WELL Building Standard-VOC Restrictions, and Living Building Challenge–Healthy Interior Performance. Contact your Tnemec representative for more information.
This product is part of a coating system tested in accordance with ISO 12944-6 (2018). Contact your Tnemec representative for coating system test results.
View more product detailsProduct Data Sheets
- English_Series_1224_Epoxoline_Wb_pds.pdf
- French_Series_1224_Epoxoline_Wb_pds.pdf
- Spanish_Series_1224_Epoxoline_Wb_pds.pdf
Safety Data Sheets
Email this productContact your sales reps for quotes, problem solving advice, extensive technical knowledge, pricing, ordering and field support.
Number of Components
Two: Part A and Part B
HAPS
0.00 lbs/gal solids
Volatile Organic Compounds
Unthinned: 0.01 lbs/gallon (1 gram/litre)
Theoretical Coverage
1,049 sq ft/gal (25.7 m²/L at 25 microns). See APPLICATION for coverage rates.
Topcoats
Series 66, 73, 113, 114, 115, V115, 156, 157, 158, 161, 180, 181, 270, 273, 280, 281, 287, 290, 297, 971, 975, 1026, 1028, 1029, 1070, 1070V, 1071, 1071V, 1072, 1072V, 1077, 1078, 1080, 1081, 1094, 1095, 1096. Note: An extended cure time is needed when topcoating with Series 297, 1080, or 1081. Reference additional recoat times listed below the cure table. Note: More than one finish coat may be required to achieve a uniform and desired gloss level.
Volume Solids
65% (mixed)
Finish
Flat
Recommended DFT
4.0 to 8.0 mils (100 to 205 microns) per coat.
Note: Two coats may be required for aggressive exposures.
Primers
Steel: Self-priming or Series 1, N69, N69F, 90G-1K97, 90-75, 90-97, H90-97, 91-H₂O, 94-H₂O, 98-H₂O, N140, N140F, 394. Note: Series 1, 90G-1K97, 90-97, H90-97, 91-H2O, 94-H2O, and 394 must be exterior exposed for one day prior to topcoating.
Galvanized Steel: Self-priming
Concrete: Self-priming, Series 215, 217, 218, 1254
CMU: Self-priming, Series 130, 215, 1254
Drywall: Self-priming
Curing Time
| Temperature | To Touch | To Handle | To Recoat† |
|---|---|---|---|
| 120°F (49°C) | 15 minutes | 1 hour | 2 hours |
| 95°F (35°C) | 30 minutes | 2 hours | 3 hours |
| 75°F (24°C) | 1 hour | 6 hours | 8 hours |
| 55°F (13°C) | 2 hours | 8 hours | 16 hours |
| 45°F (7°C) | 3 hours | 10 hours | 24 hours |
| 35°F (2°C) | 4 hours | 3 days | 4 days |
† The following minimum recoat times apply when topcoating with Series 297, 1080 or 1081: 95°F (35°C) 12 hours, 75°F (24°C) and 55°F (13°C) 24 hours, 45°F (7°C) 4 days, 35°F (2°C) 7 days. Curing time varies with surface temperature, air movement, humidity and film thickness. Substrates containing integral water repellants can prolong cure times.
Still have questions? Request the information you’re looking for:
Request InfoHow to Purchase
Tnemec coatings are sold through a select network of local independent sales representatives who can help you find the best product for your needs. Find a rep